| 特性级别 | 热稳定性|||耐高温|||耐磨|||高强度|||高流动|||高圄冲|||高光泽|||高刚性||| |
| 牌号 | PP TB52U |
| 加工级别 | 注堕级||| |
| 品名 | PP HANWHA TOTAL Hanwha TB52U |
| 厂家(产地) | 韩国三星TOTAL/韩华 |
| 用途级别 | 电子电器部件|||运动器材|||家电部件|||电动工具配件|||薄壁制品||| |
抗静电 抗紫外线PP TB52U
PP HANWHA TOTAL Hanwha TB52U
Hanwha Total PP TB52U
高结晶性聚丙烯
滑石填料
HANWHA TOTAL PETROCHEMICALS Co., Ltd.
产品说明:
TB52U is a super weatherability and heat-resistant polypropylene compound ideally suited for use in air-conditioner exterior parts and other outdoor purposes. We have significantly improved strength and heat-resistance by adding talc, the inorganic filler, to polypropylene. This product is made with a variety of base PP, such as HIPP (High Isotactic Polypropylene). In addition to the characteristics noted above TB52U exhibits excellent impact-resistance, long-term heat-resistance, resistance to thermo-discoloration, anti-static property, and dimensional stability. TB52U has received certification for environmental exposure, meeting the UL 746C F1 and UL484 standards.
抗静电 抗紫外线PP TB52U
PP HANWHA TOTAL Hanwha TB52U
填料/增强材料 |
|
添加剂 | 抗静电性紫外线稳定剂 |
特性 | 尺寸稳定性良好刚性，高高强度间苯二甲抗静电性抗撞击性，高可加工性，良好耐气候影响性能良好耐热性，高 |
用途 | 电气/电子应用领域电气元件工业应用容器室外应用外壳 |
形式 |
|
加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
密度 | 1.04 | g/cm3 | ASTM D1505 |
熔流率（熔体流动速率） (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
收缩率 - 流动 (2.00 mm) | 1.0 到 1.4 | % | ASTM D955 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
洛氏硬度 (R 级) | 93 | ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
抗张强度 3 | 34.3 | MPa | ASTM D638 |
伸长率 3 (断裂) | 60 | % | ASTM D638 |
明显的弯曲模量 | 49.0 | MPa | ASTM D747 |
弯曲模量 4 | 2650 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
悬壁梁缺口冲击强度 (23°C) | 83 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
载荷下热变形温度 (0.45 MPa, 未退火) | 139 | °C | ASTM D648 |
| 注射 | 额定值 | 单位制 | |
料筒后部温度 | 180 到 200 | °C | |
料筒中部温度 | 190 到 210 | °C | |
料筒前部温度 | 200 到 220 | °C | |
模具温度 | 40.0 到 80.0 | °C | |
注塑压力 | 58.8 到 98.1 | MPa | |
保压 | 39.2 到 88.3 | MPa | |
螺杆转速 | 30 到 80 | rpm |
抗静电 抗紫外线PP TB52U
PP HANWHA TOTAL Hanwha TB52U
PP(聚丙烯#百折胶|软胶)/TB52U/韩华道达尔
用途： 其它
特性备注：稳定性，加工性
重要参数： 熔体流动速率:12 g/10min 密度:1.04 g/cm3 成型收缩率:1.2 % 缺口冲击强度:8.5 拉伸强度:34 MPa 断裂伸长率:60 % 弯曲强度:49 MPa 弯曲模量:2648 MPa 硬度:93 热变形温度:139 ℃
生产厂商：韩华道达尔株式会社
抗静电 抗紫外线PP TB52U
PP HANWHA TOTAL Hanwha TB52U