抗撞击性ABS+PC MC8100-东莞市屹立塑胶有限公司

产品展厅

抗撞击性ABS+PC MC8100

产品详请

PC/ABS, low viscosity, high impact and ductile.

附加功能

基本信息
特性	低粘度抗撞击性，高延展性
用途	汽车领域的应用
加工方法	注射成型
多点数据	Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Compressive Stress vs. Strain (ASTM D695) Elastic Modulus vs Temperature (ASTM D4065) Flexural DMA (ASTM D4065) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835)

CYCOLOY™ MC8002 resin 物性表

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	1.13 g/cc	1.13 g/cc	ASTM D792
吸水率	0.10 % @Time 86400 sec	0.10 % @Time 24.0 hour	ASTM D570
线性成型收缩率,Flow	0.0050 - 0.0070 cm/cm @Thickness 3.20 mm	0.0050 - 0.0070 in/in @Thickness 0.126 in	SABIC Method
熔体流动速率	8.5 g/10 min @Load 5.00 kg, Temperature 260 °C	8.5 g/10 min @Load 11.0 lb, Temperature 500 °F	ASTM D1238

重要参数： 熔体流动速率:12 g/10min 密度:1.04 g/cm3 成型收缩率:0.65 % 缺口冲击强度:240 拉伸强度:35.9 MPa 断裂伸长率:18 % 弯曲强度:79.3 MPa 弯曲模量:2620 MPa 维加纤MC5215 ABS+PC

沙伯基础创新塑料Cycoloy®cy9640 PC + ABS

聚合物，热塑性塑料，ABS聚合物，聚碳酸酯/ ABS合金，无筋，聚碳酸酯（PC）

沙伯基础创新塑料（GE塑料）

电镀ABS+PC MC1300 汽车

沙伯基础创新塑料Cycoloy®fxc810ar PC + ABS

聚合物，热塑性塑料，ABS聚合物，聚碳酸酯/ ABS合金，无筋，聚碳酸酯（PC）

医疗设备HC1204HF ABS+PC

产品说明：