Hanwha Total PP BI970
高结晶性聚丙烯
HANWHA TOTAL PETROCHEMICALS Co., Ltd.
产品说明:
BI970 is a highly isotactic block copolymer with ultra-high flowability, high impact, and higher crystalinity compared to general PP. It maintains an optimum balance of strength and impact resistance due to high crystalline technology and the most appropriate rubber design. Through the control of molecular weight distribution, the product shows superior melt flow compared to normal PP and is appropriate for energy savings and multi-cavity injection molding. BI970 is useful in large scale thin products with low distortion tendencies and may also be used as a compound base resin.
特性 | · Block Copolymer· 高强度· 间苯二甲· 结晶· 抗撞击性，高· 流动性高· 耐低温冲击· 耐热性，高· 窄分子量分布
|
用途 | · 薄膜· 杯子· 汽车防撞杆· 汽车内部装备· 汽车仪表板· 容器
|
形式 | · 粒子 |
加工方法 | · 注射成型 |
物理性能 | 额定值 | 单位制 | 测试方法 |
密度 | 0.910 | g/cm3 | ASTM D1505 |
熔流率（熔体流动速率） (230°C/2.16 kg) | 100 | g/10 min | ASTM D1238 |
硬度 | 额定值 | 单位制 | 测试方法 |
洛氏硬度 (R 级) | 87 | ASTM D785 |
机械性能 | 额定值 | 单位制 | 测试方法 |
抗张强度 (屈服) | 31.4 | MPa | ASTM D638 |
伸长率 (断裂) | 25 | % | ASTM D638 |
弯曲模量 | 1670 | MPa | ASTM D790 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
悬壁梁缺口冲击强度 (23°C) | 59 | J/m | ASTM D256 |
热性能 | 额定值 | 单位制 | 测试方法 |
载荷下热变形温度 (0.45 MPa, 未退火) | 125 | °C | ASTM D648 |
光学性能 | 额定值 | 测试方法 | |
光泽度 | 85 | ASTM D2457 |
注射 | 额定值 | 单位制 | |
料筒后部温度 | 160 到 200 | °C | |
料筒中部温度 | 200 到 240 | °C | |
料筒前部温度 | 220 到 260 | °C | |
模具温度 | 30.0 到 50.0 | °C | |
注塑压力 | 98.1 到 245 | MPa | |
保压 | 78.5 到 226 | MPa |